Hastelloy c -276 av nickel-krom-molybden-legeringar som innehåller volfram
the alloy has excellent corrosion resistance to most corrosion media in oxidation and reduction states. Excellent point corrosion resistance, crevice corrosion and stress corrosion cracking performance. alloys are suitable for various chemical process industries containing oxidizing and reducing media. The high content of molybdenum and chromium enables the alloy to resist the erosion of chloride ions, and the tungsten element further improves its corrosion resistance. Hastelloy C-276 is one of the few materials that can resist the corrosion of moisture-wet chlorine gas, hypochlorite and chlorine dioxide solution. The alloy has significant corrosion resistance to high concentration of chlorinated salt solution (such as järnklorid och kopparklorid) .
Hastelloy c -276 motsvarande nummer motsvarande
|
Kategori |
Generalnamn |
Antal tyska märken |
Enhetligt digitalt nummernummer |
|
Ni-cr-mo |
Hastelloy c -276 54 ni16mo15cr |
2.4686 |
Hastelloy C -276 Motsvarande gjutning och bar betyg
|
Gjutning |
Förlåtelser (liknande deformerade legeringar) |
Bar |
|||
|
Specifikation nr . |
Licens |
Specifikation nr . |
Licens |
Specifikation nr . |
Licens |
|
ASTM A 494 |
Cw -2 m |
ASTM B 462astm B 564 |
N10276 |
B 574 |
N10276 |
Hastelloy c -276 andra märken motsvarande
|
Namn |
Gb i Kina |
ASTM i USA |
Din Tyskland |
Brittisk BS |
Afnor Frankrike |
|||||||||
|
Nyvaror |
Gammal varumärke |
|||||||||||||
|
Hastelloy c -276 |
NS3304 |
Ns334 |
UNS N10276 |
W . nr .2.4819 (NIMO16CR15W) |
Nc17d |
|||||||||
|
Hastelloy c -276 fysiska egenskaper |
||||||||||||||
|
Densitet |
Smältpunkt |
Termisk konduktivitet |
Specifik värmekapacitet |
Elastisk modul |
Skjuvmodul |
resistivitet |
Poissons förhållande |
Linjeutvidgningskoefficient |
||||||
|
g/cm3 |
grad |
λ/(w/m • examen) |
J/kg • examen |
Gpa |
Gpa |
μΩ•m |
a/10-6 examen -1 |
|||||||
|
8.9 |
1325 |
10.2 (100 grader) |
407 |
208 |
79 |
1.25 |
11.7 (20 ~ 100 grader) |
|||||||
|
1370 |
||||||||||||||
Hastelloy c -276 kemisk sammansättning
|
Licens |
Uns no . |
Kemiskt element% |
C |
Mn |
Si |
P |
S |
Mo |
Fe |
Ni |
Hp |
KSI [MPA] av minsta draghållfasthet |
Minsta avkastningsstyrka KSI [MPA] |
Minsta förlängning,% mätare 2 tum [50 mm] |
|
Cw2m |
N26455 |
Max |
0.02 |
1.00 |
0.80 |
0.03 |
0.03 |
15.0-17.5 |
2.0 |
Balans |
15.0-17.5 |
72[495] |
40[275] |
20 |
Hastelloy C -276 Temperaturintervall
|
Generalnamn |
Specifikation nr . |
Licens |
Temperaturområde |
|
Hastelloy c -276 |
ASTM B 564 |
N10276 |
Lämplig temperatur mindre än eller lika med 675 grader, flänsens slutventil mindre än eller lika med 538 grader Använd endast fast lösningsmaterial |
Hastelloy C -276 Värmebehandlingskrav
|
Licens |
Värmebehandlingskrav |
|
Cw -2 m |
Värm upp till mer än 1175 grader, håll tillräckligt med tid för att värma gjutningen till denna temperatur, släcka den i vatten eller på annat sätt släcka det . |
Hastelloy C -276 Korrosionsegenskaper
|
Medium |
|
Korrosion av oxidationssyror såsom salpetersyra, salpetersyra och svavelsyra, blandad syra, gallinsyra och svavelsyra, samt korrosion av oxidationssalter eller media som innehåller andra oxidanter såsom hypoklorit vid högre temperaturer än normal temperatur |
|
God korrosionsbeständighet mot havsvatten, ättiksyra, våtklor, kan också användas i klor eller klorerade medier . Men korrosionsbeständigheten hos nickelmolybdenlegering i saltsyra är inte lika bra som för nickelmolybden -legering .} |
|
Bra korrosionsbeständighet i fall av oxidation, reduktion och halogenjoner |
|
Hastelloy c -4 av hydrofluorinsyra har lägre korrosionshastighet än hastelloy c -276. |